Purpose of this study is to obtain failure modes and failure loads of two Parallel pin loaded holes in unidirectional glass fibre/epoxy by adding nanoclay in the absence of nanoclay composite laminates using finite element analysis; the results are validated through experiment. The geometrical parameters studies in this survey include the distance between the diameter of the hole (e/d) and the free edge of specimen, the distance between two holes-to-hole diameter (M/d). The samples were exposed to constant speed tensile loading. The results showed that by adding nanoclay, failure load increases and failure modes varies from shear out to bearing failure. Furthermore, increasing distance from the free edge of the pin centre’s increases load bearing capacity of two type of composite materials and changes the failure mode from shear to the bear, it increases and decreases the distance from canter’s of pin in layers with and without nanoclay particles, respectively and changes failure mode from shear to bear mode. In order to find morphology of specimens and dispersion quality, Scanning Electron Microscope (SEM) was used. For predicting failure load and differentiating failure modes, Tsai-hill failure criteria associated with material property degradation is used. Experimental and FEM results indicate importance of considering the impact of e/d and M/d ratios in the design of two Parallel pin joints. ANSYS was used to carry out numerical simulation and the results denote a good agreement between numerical and experimental results. In this study, by designing an experimental and numerical procedure to estimate the effect of nanoclay, on failure mode and failure load of typical composite material, glass-epoxy, we could illustrate that adding nanoclay brought with it improvement of shear and tensional strength of glass-epoxy about 10 %.


[1]     Agarwal, B. L., Static Strength Prediction of Bolted Joint in Composite Material, AIAA Journal, Vol. 18, No. 11, 1980, pp. 1371-1375.
[2]     Camanho, P.P., Matthews, F. L., Stress Analysis and Strength Prediction of Mechanically Fastened Joints in FRP: a Review, Composites Part A, Vol. 28, No. 6, 1997, pp. 529-547.
[3]     Abd-El-Naby S. F. M., Hollaway, L., The Experimental Behavior of Bolted Joints in Pultruded Glass/Polyester Material, Part 1: Single-bolt joints, Journal of Composite Materials, Vol. 24, No. 7, 1993, pp. 531-538.
[4]      Man-Wai, H., Chun-Ki, L., Kin-tak, L., Dickon, H. L. Ng., and David, H., Mechanical Properties of Epoxy-Based Composites Using Nanoclays, Composite Structures, Vol. 75, 2006, pp. 415-421.
[5]     Gupta, N., Chih Lin, T., and Shapiro, M., Clay-Epoxy Nanocomposites: Processing and Properties, Journal of Mineral, Metal and Materials, Vol. 75, 2007, pp. 61-65.
[6]     Subramaniyan, A. K., Sun, C. T., Enhancing Compressive Strength of Unidirectional Polymeric Composites Using Nanoclay Composites: Part A, Vol. 37, No. 12, 2006, pp. 2257-2268.
[7]     Sekhon, M., Bhunia, H., and Saini, J. S., Effect of Ply Orientation On Strength and Failure Mode of Pin Jointed Unidirectional Glass-Epoxy Nanoclay Laminates, Defence Science Journal, Vol. 65, 2015, pp. 489-499.
[8]     Suresh Babu, V., Tara Sasanka, C., and Ravindra, K., Failure and Stress Analysis of Glass Fiber Reinforced Laminated Composite Pinned Joints, Int J Advanced Design and Manufacturing Technology, Vol. 6, 2013, pp. 13-19.
[9]     Khashaba, U. A., Sebaey, T. A., and Alnefaie, K. A., Failure and Reliability Analysis of Pinned-Joint Composite Laminates: Effects of Pin–Hole Clearance, Journal of Composite Materials, Vol. 47, No.18, 2012, pp. 2287-2298.
[10]  Hyer, M. W., Klang, E. C., and Cooper, D. E., The Effects of Pin Elasticity, Clearance, and Friction On the Stresses in A Pin-Loaded Orthotropic Plate, Journal of Composite Materials, Vol. 21, No. 3, 1987, pp. 190-206.
[11]  Jong, T. D., Stresses Around Pin-Loaded Holes in Elastically Orthotropic or Isotropic Plates, Journal of Composite Materials, Vol. 11, No. 3, 1977, pp. 313-331.
[12]  Shishesaz, M., Attar, M. M., and Robati, H., The Effect of Fiber Arrangement On Stress Concentration Around a Pin in A Laminated Composite Joint, ASME 2010 10th Biennial Conference on engineering systems design and Analysis, 2010.
[13]  Singh, M., Saini, J. S., and Bhunia, H., Investigation on Failure Modes for Pin Joints Made from Unidirectional Glass-Epoxy Nanoclay Laminates, Fatigue & Fracture of Engineering Materials & Structures, Vol 39, No. 3, 2015, pp. 320-334.
[14]  shishesaz, M., Attar, M. M., Stress Concentration Analysis of Fiber-Reinforced Multilayered Composites with Two Serial Pin-Load Holes, 18th Annual Conference of Mechanical Engineering, 2011.
[15]  Sekhon, M., Saini, J. S., Singla, G., and Bhunia, H., Influence of Nanoparticle Fillers Content On the Bearing Strength Behavior of Glass Fiber-Reinforced Epoxy Composites Pin Joints, Proceedings of the Institution of Mechanical Engineers Part L: Journal of Materials: Design and Applications, Vol. 1, 2015.
[16]  Attar, M. M., Barati, F., Ahmadpour, M., and Rezapour, E., Failure Analysis of Unidirectional Polymeric Matrix Composites with Two Serial Pin Loaded-Holes, Journal of Mechanical Science and Technology, Vol. 30, No. 6, 2016, pp. 2583-2591.
[17]  Nanda Kishore, A., Malhotra, S. K.  and Siva Prasad, N., Failure Analysis of Multi-Pin Joints in Glass Fibre/Epoxy Composite Laminates, Composite Structures, Vol. 9, 2009, pp. 266-277.
[18]  Dehghanpour, S., Hosseini Safari, K., Barati, F., and Attar, M. M., Stress Concentration Around of Pin-Loaded Hole in Unidirectional Multi-Layered Metallic Matrix Composite Material, Journal of Mechanical Science and Technology, Vol. 33, No. 10, 2019, pp. 4891-4898.
[19]   Karakuzu, R., Taylak, N., Murat Icten, B., and Aktas, M., Effects of Geometric Parameters On Failure Behavior in Laminated Composite Plates with Two Parallel Pin-Loaded Holes, Journal of Composite Structures, Vol. 85, 2008, pp. 1-9.
[20]  ASTM D3410 / D3410M – 16, Standard Test Method for Compressive Properties of Polymer Matrix Composite Materials with Unsupported Gage Section by Shear Loading.